lightweight autoclaved aerated concrete brick sales Sri Lanka Philippines Indonesia Malaysia Vietnam Thailand Mongolia India
Product Description
light weight autoclaved aerated concrete brick sales Sri Lanka Philippines Indonesia Malaysia Vietnam Thailand Mongolia India
1.Introduction
Areated concrete brick (light brick ) is the light and porous buidling material. It has light weight keeping temperature can't burn and other advantages.it can be made into many kinds of bricks(for example:600×200×100,80×80×180,240×115×53,600×200×125),they could be used industry building and common building.they are more and more popular in the world.in the future,they will replace the Clay brick completely.
2.Areated concrete common conception
Common concrete density is usually 1600-2400kg/m3,but Areated concrete are 500kg/m3,600kg/m3,700kg/m3.It has not the big grain,main use silicon material (for example:coal ash,sand,stone dust and others ),through making the material small for example sand,they can be used directly if has enough degree of small (for example coal ash.Mixing calcium material lime cement water to a special slop,then add the aluminum dust and the additive.Make the aluminum dust and the special slop have a Chemical reflect.then produce Hydrogen to make the concrete slop to expanding or swell,foam.Next,put them into the curing room to concreting cutting steaming curing,last,there will bacome the light brick,the porous rate is 70-80%.
3.Advantages
1)light weight
Areated concrete density is usually 400-700kg/m3,(according the market in produce ),same as 1/3 of clay brick and 1/5 common concrete.So use the Light brick can reduce the weight of the build more,and also reduce the beam of roof and pillar press best.then you can see,it can save the material and cost,it also fighting shaking.
2)keeping temperature
It has many porous,the delivery hearting coefficient is 0.9-0.22W/(mk),the same as 1/4 or 1/5 of clay brick,so it is best materials now in the world. Also many kinds raw material,have lowest wasteMain Material:coal ash sand waste mine material coal stone,stone dust and other silicon materials.
4.Detailed Product Description
1)Foam block machine,best offer with most competitive price ,quality guarantee machine, any size block widely used for high buildings,walls, etc many many infrastructure projects.
2)We are the top leader in China on manufacturing the Autoclaved Aerated Concrete Line(AAC) with 65% market share. We have exported our lines to different countries -- Russia, Thailand, Ukraine, Middle East and so on.
3)We can supply our customer for designning, production, installation, commissioning, training and good after-sale service.
4)Capacity: from 50000 cubic meter to 300,000 cubic meters per year.
5)Equipments: stocking raw materials, mixing, molding, forming, cutting, evaporating and curing, crane cramp, transporting etc.
5.AAC Production Line/Autoclaved Aerated Concrete Production Line
1)Product weight is according to 600kg/m3 to control.
2)annual capacity 300,000M3.
3)set raw material proportion: cement 6.5%, raw lime 23%, flyash 68%, gypsum 3%, aluminum paste powder 350g/M3.
4)water and material rate 0.631
5)one mould product 2.88M3
6)Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.
7)casting slurry temperature 38-42 degree
8)body quiet stop. Time is 1.5-2.5hours, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa
9)Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.
10) Cement lime fly ash style aerated block raw material proportion
| name | unit | proportion |
| flash | % | 65-70 |
| cement | % | 6-15 |
| lime | % | 18-25 |
| gypsum | % | 3-5 |
| Aluminum powder paste(600kg/m3) | 1/10000 | 8 |
| Water & material rate |
| 0.60-0.65 |
| Casting system | OC | 36-40 |
| Aluminum mixing time | S | 30-40 |
11)Cement lime Sand style aerated block raw material proportion
| Name | Unit | proportion |
| Sand | % | 55-65 |
| Cement | % | 10-20 |
| Lime | % | 20-30 |
| Gypsum | % | 2-3 |
| Aluminum powder paste(600kg/m3) | 1/10000 | 8 |
| Water & material rate |
| 0.65-0.75 |
| Casting system | OC | 35-38 |
| Aluminum mixing time | S | 30-40 |
Reference: cement is 42.5 Portland or 42.5 common cement
Aluminum power paste calculate to use according to 600kg/m3
Remark: the accurate batching rate is adjustable according to the raw material locally
1)Cross Cutting - AAC
Transverse Cutting Machine
| Size | Min Spacing of Wires | Range of Oscillation(mm) | Diameter of Cutting Wire(mm) | Length(mm) | Width(mm) | Height(mm) |
| 4.2*1.2*0.6 | 10mm | 7.5 | 0.6-1.0 | 5200 | 3200 | 3560 |
| 4.8*1.2*0.6 | 10mm | 7.5 | 0.6-1.0 | 5900 | 3200 | 3560 |
| 6.0*1.2*0.6 | 10mm | 7.5 | 0.6-1.0 | 7200 | 3200 | 3560 |
2)Vertical Cutting - AAC
Longitudinal Cuttting Machine
| Size | Min Spacing of Wires | for Horizintal Cutting(mm) | for Side Trimming(mm) | Length(mm) | Width(mm) | Height(mm) |
| 4.2*1.2*0.6 | 5mm | 0.6-0.8 | 0.8 | 5500 | 2860 | 2500 |
| 4.8*1.2*0.6 | 5mm | 0.6-0.8 | 0.8 | 5500 | 2860 | 2500 |
| 6.0*1.2*0.6 | 5mm | 0.6-0.8 | 0.8 | 6500 | 2860 | 2500 |
3)Cutting Trolley(frequency conversion cutting trolley)
| Size(m) | Max Traveling Speed | Reductor(Brake Motor) | Length(mm) | Width(mm) | Height(mm) |
| 4.2*1.2*0.6 | 17.5m/min | GS77-Y3-4P-28.41-M3 | 3600 | 1700 | 1160 |
| 4.8*1.2*0.6 | 17.5m/min | GS77-Y3-4P-28.41-M3 | 4200 | 1700 | 1160 |
| 6.0*1.2*0.6 | 17.5m/min | GS77-Y3-4P-28.41-M3 | 5400 | 1700 | 1160 |
4)Cuttting rail - AAC
Our Factory and Workshop